?dezincification

dezincification 發(fā)音

英：[di?z??k?f??ke??n]　　美：[di??z??k?f??ke??(?)n]

英：　　美：

dezincification 中文意思翻譯

dezincification 短語(yǔ)詞組

1、dezincification resistant ─── 抗脫鋅

2、dezincification process ─── 脫鋅工藝

3、dezincification of bronze ─── 青銅脫鋅

4、dezincification pictures ─── 脫鋅圖片

5、dezincification brass ─── 脫鋅黃銅

6、dezincification pex ─── 脫鋅pex

7、dezincification pdf ─── 脫鋅pdf

8、dezincification lawsuits ─── 脫鋅訴訟

dezincification 相似詞語(yǔ)短語(yǔ)

1、damnification ─── n.[法]損傷；損害

2、zincification ─── n.鍍鋅；鍍鋅法

3、densification ─── n.密實(shí)化；封嚴；[化學(xué)]稠化

4、devitrification ─── n.使不透明；除去玻璃光澤

5、zinkification ─── 鋅化作用

6、zinckification ─── 鍍鋅

7、resinification ─── n.樹(shù)脂化；以樹(shù)脂處理

8、denitrification ─── n.脫氮；[化學(xué)]反硝化作用

9、decalcification ─── n.脫鈣作用

dezincification 常見(jiàn)例句（雙語(yǔ)使用場(chǎng)景）

1、ADVANCES IN RESEARCHES OF DEZINCIFICATION MECHANISM OF BRASS ─── 黃銅脫鋅腐蝕的研究進(jìn)展

2、dezincification rate ─── 脫鋅率

3、Keywords Brass dezincification;Positron lifetime;Vacancy; ─── 黃銅脫鋅;正電子壽命;空位;

4、Dezincification selectively removes zinc from the alloy, leaving behind a porous, copper-rich structure that has little mechanical strength. ─── 脫鋅現象有選擇的從合金中去除鋅元素，造成多孔、富銅結構，降低了機械強度。

5、The effect of increasing strain rate on the increase of dezincification coefficient was diminished with increase in potential. ─── 應變速率的加快對增加脫鋅系數的作用也隨電位提高而減弱。

6、Dezincification selectively removes zinc from the alloy, leaving behind a porous, copper-rich structure that has little mechanical strength. ─── 脫鋅現象有選擇的從合金中去除鋅元素，造成多孔、富銅結構，降低了機械強度。

7、Keywords hydrocyclone;separation;dezincification;engineering design; ─── 關(guān)鍵詞水力旋流;分離;脫鋅;工程設計;

8、Abstr: the mechanism and various influence factors of the galvanized sheet dezincification is briefly reviewed. ─── 文章摘要：簡(jiǎn)要闡述鍍鋅板脫鋅機理及多種影響因素。

9、ON THE VOLUME DIFFUSION MECHANISM DURING DEZINCIFICATION OF BRASS ─── 黃銅脫鋅體擴散機制研究

10、Finally, the mechanism of dezincification related to the SCC of brass in nitrate solution is discussed. ─── 文中還討論了黃銅在亞硝酸鹽溶液中SCC過(guò)程的脫鋅機理。

11、Determination of dezincification resistance of brass ─── 黃銅脫鋅

12、EPMA Analysis of the Dezincification Corrosion of Condenser Copper Alloy Tubes ─── 電廠(chǎng)凝汽器銅管脫鋅腐蝕的電子探針?lè )治?/p>

13、An in serveice valve suffering from Dezincification has a white powdery substance of mineral stains on its exterior surface. ─── 應用中的閥門(mén)如果出現脫鋅現象，在產(chǎn)品表面就會(huì )出現粉狀物質(zhì)或礦物污點(diǎn)。

14、As a standard NIBCO bronze/brass balancing valves are made to be “Dezincification Resistant,” which is a seal of quality and longevity. ─── 作為標準，美國尼伯科青銅/黃銅平衡閥由“抗脫鋅”材料制造，是一種優(yōu)質(zhì)和耐用的密封材料。

15、DIFFUSION MECHANISM OF DEZINCIFICATION IN DOUBLE-PHASE BRASS EXPOSED TO SEAWATER ─── 實(shí)海暴露雙相黃銅脫鋅的擴散機制

16、The results showed that localized anodic dissolution is the essential cause of SCC, while considerable dezincification enhanced the suseptibility to cracking. ─── 結果說(shuō)明,包含銅在內的局部陽(yáng)極溶解是該體系SCC的根本原因,而大量的脫鋅則加劇了開(kāi)裂敏感性。

17、dezincification corrosion resistance ─── 耐脫鋅腐蝕

18、Keywords steam condenser;dezincification corrosion;EMPA; ─── 關(guān)鍵詞凝汽器;脫鋅腐蝕;電子探針;

19、ADVANCES OF RESEARCHES ON THE DEZINCIFICATION MECHANISM OF BRASS ─── 黃銅脫鋅腐蝕機理的研究進(jìn)展

20、Due to the synergetic effect of boron and arsenic, dezincification was hindered. ─── 硼能填充鋁黃銅中的雙空位，減緩鋅的溶解速率；

21、The results show that the main cause of the original corrosion leakage of H68A condenser brass copper tubes is dezincification and. ─── 結果表明,造成H68A凝汽器黃銅管腐蝕泄漏的主要原因是脫鋅腐蝕。

22、To begin with the phenomenon and characteristics of dezincification of brass, the review is made on the mechanisms, prevention and influence factors of dezincification. ─── 從黃銅脫鋅的現象、特征及其影響因素出發(fā)，對黃銅脫鋅的優(yōu)先溶解機制、溶解-再沉積機制、雙空位機制和滲流機制等進(jìn)行了描述。

23、Effect of hydrogen on stress induced by dezincification layer on brass ─── 氫對黃銅脫鋅層引起拉應力的影響

24、Dezincification of duplex brass, which is a form of corrosion, may occur when in contact with certain aggressive waters. ─── 兩相黃銅的脫鋅現象,是一種腐蝕,當接觸到某些侵蝕性水時(shí)可能發(fā)生。

25、dezincification preventive substance ─── 脫鋅防止劑

26、Dezincification selectively removes zinc from the alloy, laving behind a porous.Copper-rich structure that has little mechanical strength. ─── 脫鋅 現象有選擇的從合金中去除鋅元素,造成多孔、富銅結構，降低了機械強度。

27、As a standard NIBCO bronze fire protection valves are made to be "Dezincification Resistant," which is a seal of quality and longevity. ─── 作為一種基本要求，美國尼伯科青銅消防閥門(mén)都具有“抗失鋅”特性，質(zhì)量更加優(yōu)異，使用壽命更加長(cháng)。

28、Dezincification resistant silicon bronze stem ─── 脫鋅防腐蝕硅青銅閥桿

29、The effect of increasing sttrain rate on the increase of dezincification coefficient was diminished with increase in potential. ─── 應變速率的加快對增加脫鋅系數的作用也隨電位提高而減弱。

30、Valves shall be manufactured from dezincification resistant brass or bronze rated 240 psi at 250 f. ─── 閥門(mén)材質(zhì)應該是抗失鋅現象的黃銅或青銅,壓力－溫度等級為121℃,240 psi。

31、The strain rate at the crack tip for the maximum dezincification coefficient was approximately 4 times as high as initially applied strain rate. ─── 在穩態(tài)擴展階段,裂紋尖端導致最大脫鋅系數的應變速率估計約為初始應變速率的4倍左右。

32、Keywords dezincification;H68A brass tube;leakage; ─── 脫鋅腐蝕;H68A銅管;泄漏;

33、Dezincification of duplex brass , which is a form of corrosion. may occur when in contact with cart ain aggressive waters. ─── 兩相黃銅脫鋅現象,是一種腐蝕,當接觸到某些侵蝕性水時(shí)可能發(fā)生.

34、To overcame the problem special copper alloy.Which contain an inhibitor and undergo heat treatment, have been developed which are assistant to corrosion by dezincification. ─── 為了解決這個(gè)問(wèn)題，特殊的銅合金包含防蝕劑，并經(jīng)過(guò)熱處理，已經(jīng)可以抵抗脫鋅的腐蝕。

35、The failure was caused by dezincification corrosion. ─── 結果表明：凝汽器銅管的腐蝕屬栓狀脫鋅腐蝕。

36、dezincification corrosion ─── 脫鋅腐蝕

37、Through the reduction roasting, the dezincification rate reached up to 98%, a high grade iron ore with only 0. ─── 通過(guò)還原焙燒，高爐塵泥脫鋅率可達98%，并得到含鋅率僅為0。

38、The results show that the main cause of the original corrosion leakage of H68A condenser brass copper tubes is dezincification and. ─── 結果表明，造成H68A凝汽器黃銅管腐蝕泄漏的主要原因是脫鋅腐蝕。

39、29. To overcome the problem special copper alloys, which contain an inhibitor and undergo heat treatment, have been developed which are resistant to corrosion by dezincification. ─── 為了解決這個(gè)問(wèn)題，已經(jīng)開(kāi)發(fā)出一種特殊的銅合金，內含一種抑制成分，并經(jīng)過(guò)熱處理，能夠抵御脫鋅現象的侵蝕。

40、The further development prospects in the application of RE elements to preventing dezincification were presented. ─── 重點(diǎn)敘述了微量稀土元素在抑制黃銅脫鋅腐蝕中的作用機理和其具有的發(fā)展前景。

41、Keywords corrosions;dezincification;rubefaction;welding temperature;overburn.; ─── 腐蝕;脫鋅;發(fā)紅;焊接溫度;過(guò)燒;

42、Keywords condenser;brass pipe;corrosion;dezincification;mechanism; ─── 凝汽器;黃銅管;腐蝕;脫鋅;機理;

43、The physical attributes of an in-service valve with Dezincification includes a white powdery substance or mineral stains on its exterior surface. ─── 使用中的閥門(mén)出現失鋅想象時(shí)的物理特征包括：在外表面出現白色粉末或礦物污點(diǎn)。

44、Dezincification is normally associated with brass valves where the zinc content exceeds 15%. ─── 脫鋅現象通常發(fā)生在鋅含量超過(guò)15%的黃銅閥門(mén)上。

45、Study on Dezincification of Dust Contained Zinc in Lab ─── 含鋅粉塵脫鋅處理的實(shí)驗室研究

46、The role of boron in inhibiting dezincification of aluminium brass was investigated by ICP, XRD,EMPA and PAT methods. ─── 采用ICP，XRD，EMPA，PAT等方法研究了加硼對鋁黃銅脫鋅行為的影響和機理。

47、Keywords unleaded brass;dezincification;cold-deformation amount;annealing treatment; ─── 無(wú)鉛黃銅;脫鋅腐蝕;冷變形;退火熱處理;

48、Inhibition of Dezincification of Brass ─── 黃銅脫鋅的抑制

49、Dezincification resistant silicon bronze or 316SS stem ─── 脫鋅防腐蝕硅青銅或316不銹鋼閥桿

50、The results show that the failure of oil-cooler is bolt-like dezincification corrosion. ─── 結果表明,冷油器銅管的腐蝕屬于栓狀脫鋅腐蝕。

51、An in service valve suffering from Dezincification has a white powdery substance or mineral stains on its exterior surface. ─── 應用中的閥門(mén)如果出現脫鋅現象，在產(chǎn)品表面就會(huì )出現粉狀物質(zhì)或礦物污點(diǎn)。

52、As a standard NIBCO bronze fire protection valves are made to be " Dezincification Resistant, " which is a seal of quality and longevity. ─── 作為一種基本要求，美國尼伯科青銅消防閥門(mén)都具有“抗失鋅”特性，質(zhì)量更加優(yōu)異，使用壽命更加長(cháng)。

53、Dezincification is a type of corrosion in which brass dissolves as an alloy and the copper constituent redeposits from solution onto the surface of the brass as a metal, but in the porous form. ─── 脫鋅現象是一種類(lèi)型的腐蝕，黃銅作為合金溶解成銅元素，然后從溶液中在作為金屬沉積在黃銅表面，但是這種沉積卻是多孔滲水的。

54、Dezincification resistant cast bronze body and end piece ─── 耐脫鋅現象鑄青銅閥體和端口連接件

55、Keywords brass;dezincification corrosion;mechanism;RE element; ─── 黃銅;脫鋅腐蝕;機制;稀土元素;

56、"High Copper, Low Zinc Brass Castings for Dezincification Resistance" ─── 鋅含量低的高純度的銅鑄件,有效防止鋅泄漏

57、The results show that the failure of oil-cooler is bolt-like dezincification corrosion. ─── 結果表明，冷油器銅管的腐蝕屬于栓狀脫鋅腐蝕。

58、Copper-zinc alloys--Determination of dezincification corrosion resistance ─── 黃銅耐脫鋅腐蝕性能的測定

59、Dezincification of duplex brass, which is a form of corrosion, may occur when in contact with certain aggressive waters. ─── 兩相黃銅的脫鋅現象，是一種腐蝕，當接觸到某些侵蝕性水時(shí)可能發(fā)生。

60、Keywords Dezincification of brass;Volume diffusion;Positron lifetime;Divacancies; ─── 黃銅脫鋅;體擴散;正電子壽命;雙空位;

61、Keywords Brass;Dezincification;Mechanism;RE element; ─── 黃銅;脫鋅;機制;稀土元素;

62、Dezincification of Brass Tube in Condenser ─── 凝汽器銅管脫鋅腐蝕的研究

63、Keywords brass dezincification;inhibition effect;arsenic;inhibitor; ─── 黃銅脫鋅;抑制作用;砷;緩蝕劑;

64、Keywords HSn70-1CB alloy;corrosion resistance;dezincification;Ce and B; ─── 1CB合金;耐腐蝕性;脫鋅;鈰和硼;

65、Keywords Cu-based shape memory alloy;physiological saline solution;dezincification;corrosion resistance; ─── 銅基形狀記憶合金;人工體液;脫鋅腐蝕;耐蝕性;

66、An in-service valve suffering from Dezincification has a white powdery substance or mineral stains on its exterior surface. ─── 使用中的閥門(mén)如果遭遇脫鋅侵蝕，會(huì )在閥門(mén)外表產(chǎn)生白色粉末或礦物污點(diǎn)。